HN-302  Stable Agent                     40~60g/L

HN-303 make-up salt                      80~120mL/L

HN-304  stabilizer                            380~420g/L

wetting agent                                  1~3mL/L

Cr                                                    23 ~ 27g/L

Proportion                                       26 ~ 30  oBeˊ

Tem                                                 25~35℃

pH Value                                          2.0 ~ 3.0

Cathode Current Density                 6~22A/dm2

1. It’s green product without haxavalent chromium; the waste disposal is simple.

2. The coating  color is  uniform  and  bright   with  good   cover ability and distribution.

3. Compared  to  traditional   trivalent   chromium  the coating is whiter and harder, and has greater wear

resistance.

4. Current efficiency can achieve 30% while plating; Deposition rate is faster than that of haxavalent

chromium.

5. The working bath is stable  with good  impurity resistance, a better alternative to traditional haxavalent 

process.