Rack plating composition:

 Zinc oxide                                6~12g/L

 Sodium hydroxide                   100~140g/L

 Brightener HN -NH1                 8 ~12mL/L

 Brightener HN -NH2                 8~12mL/L

 Refiner HN -Nh3                      5~10mL/L   

 Temperature                          15~40℃

 Current density                       0.5~8A/dm2

 Voltage                                   2~6V

 Barrel plating composition:

 Zinc oxide                               8~12g/L

 Sodium hydroxide                  110~140g/L

 Brightener HN -Nh1                12mL/L

 Brightener HN -Nh2                8mL/L

 Refiner HN -Nh3                     5~10mL/L

 Temperature                          15~40℃

 Current density                      0.5~2A/dm2

 Voltage                                  6~12V

 Consumption:

 Brightener HN -NH1               50~100mL/1000A.H

 Brightener HN -NH2               40~80mL/1000A.H 

 Refiner HN -Nh3                    10~20mL/1000A.H

1. Non-cyanide.

2. Suitable for rack plating and barrel plating.

3. Obtain bright and esthetic deposit in a wide range of current density.

4. Even thickness of deposit, excellent dispersive ability.

5. The deposit is very soft, easy to do chromate passivation. It can be treated to other shapes after plating.

6. The process is stable, high tolerance against impurities, good temperature resistance.