LC-M72 Semi-Bright Nickel Plating
Commodity Name
LC-M72 Semi-Bright Nickel Plating
Composition and Working Conditions
|
Nickel sulfate
Nickel chloride
Boric acid
Softener LC-M71
Leveler LC-M72
Stabilizer LC-M73
Wetting agent HN-17
Temperature
pH value
Current density
Agitation
Filtration
Consumption:
Softener LC-M71
Leveling agent LC-M72
Stabilizer LC-M73
|
240~300g/L
45~55g/L
40~50g/L
4~6mL/L
0.4~0.6mL/L
0.4~0.6mL/L
1~2mL/L
45~55℃
4.0~4.8
2~6 A/dm2
Air agitation or mechanical agitation
Continuous cycle filtration
40~60 mL/1000A.H
130~200mL/1000A.H
30~50 mL/1000A.H
|
Application and Advantage
1. The sulfur content in deposit is low. Potential difference between semi-bright nickel layer and bright
nickel layer is 120~145 mV. The corrosion resistance of deposit is excellent.
2. Good flexibility, excellent leveling.
3. No coumarin in the bath, less decomposed products, The plating bath is stable and is easy to control.
4. Low production cost, economical and practical.