Hot immersion:

HN -DCR                     30~50mL/L

Temperature              70~90℃

Time                           3~10 minutes

Agitation                     Proper shaking

Ultrasonic hot immersion:

HN -DCR                    10~30mL/L

Temperature              60~80℃

Time                           1~5 minutes

Agitation                     Non- shaking

1. Suitable for all kinds of metal basal parts, such as steel, aluminum alloy, zinc die cast parts etc.

2. It is a kind of neutral active solution and wont corrode basal parts. It can remove wax quickly with its 

excellent wettability and infiltrability.

3. Less foam. Hydrophobic film is formed on surface after treatment and has a certain self-protective 

ability, which can use degreaser (pH≧11) to remove.